For quick transactions, only those who can contact us within 24 hours after the end of the auction and can make payments within 3 days should bid. Unfortunately, if you can not protect it, we will delete it at the convenience of the successful bidder.There are many people who say that the evaluation after transactions is not needed recently, so we only put it in those who have received the evaluation here to prevent mistakes. This product will be a warehouse.Asahi Kasei Wacker Silicone M4503 High strength Standard curing type 10kg set Silicone, molding silicon
It's a peaceful Made in Japan. The curing agent is a standard curing type. A set of 1kg x 10 and a hardening agent 40g x 10.. It will be the amount of the 10kg set. The shipping cost (other than Okinawa and Hokkaido) is uniform nationwide \ 3,000.-. (Not included)
Okinawa and Hokkaido are uniform \ 3,800.-Shipping may be shipped in western part, Fukuyama, tonami traffic, etc., so it is not possible to specify time.. We will ship it on business days after payment confirmation. (Closed on Saturdays, Sundays, and holidays)
(It may be delayed depending on the convenience of work such as business trip) We have enough stock, but we sell it at actual stores and our own websites.
If your order is concentrated, it may take up to 2 weeks to ship.. Long -term holidays such as weekends, holidays, GW, Obon, New Year holidays, etc. are not available, so thank you..If you subdivide after opening, the preservation stability will fall, so it is an unopened new product that remains shipped. As a main feature
Excellent liquidity
Low hardness (SHORE A about 25)
High tear intensity 22 n/mm (3-4 times torn intensity of general molding)
High flexibility and elasticity
Various types of resin (polyurethane, epoxy, PVC sol), an excellent durability for polyester resin. I will give you. The catalog is written at the bottom of this product description. There are two types of curing agents: standard type and fast -sticlated type. The fast -sticlated type is claimed to be about half of the standard type, but the time from stirring to pouring is considerably shorter.
It is said that the fast -carcified type is difficult to handle except for midwinter.. If you are not confident in the fast -sungling type, we recommend that you increase the standard curing agent and mix. For quick transactions, only those who can contact us within 24 hours after the end of the auction and can make a payment within 3 days (excluding weekends and holidays). Unfortunately, if you can not protect it, we will delete it at the convenience of the successful bidder. Please note that if you look at new people and evaluations, etc., you may be deleted due to the highest bidder convenience judged here.. (In this case, it is automatically worse than the Yahoo! system.. )
Please use no claim no return.The product description is as easy to understand as possible, but please ask after asking questions about the points you are interested in.The following catalog value.
Before curing (representative value)
Appearance white
Vehicle 23 ℃ B -type rotation viscosometer MPAS 45,000
Density 23 ℃ 1.16 g/
After curing (representative value)
23 ° C, relative humidity 50%atmosphere 96 hours later
Appearance white
Density 23 ° C, din 53479 a 1.17 g/
Hardness DIN 53505 SHORE A 25
Tensile intensity DIN 53504 S3 N/mm 5.0
Breaking stretch DIN 53504 S3 % 350
Fissure strength ASTM D624, B n/mm> 22
7 days later% <0.5
Liner heat expansion coefficient 0-150 ° C M/M K 2.0 x 10-4
Processing characteristics (representative value)
Standard curing conditions 23 ° C, relative humidity 50%mixing ratioM4503: Catalyst T40 = 100: 3 ~ 4
After mixed viscosity 40,000 [MPAS]
Work time 60-20 minutes (m4503: cat.t40 = 100: 3-4) standard type
20-5 minutes (M4503: CAT.T = 100: 1.5-2.5) Sapping type
Casting time (thickness 1cm) about 16-12 hours (M4503: cat.t40 = 100: 3-4) Standard type
About 8-2 hours (m4503: cat.t = 100: 1.5 to 2.5